首頁 >> 公司新聞 >>施工必看 >> 玻化微珠保溫砂漿施工8點注意事項
详细内容

玻化微珠保溫砂漿施工8點注意事項

时间:2016-07-18     作者:www.vfeqvs.com【原创】   阅读


玻化微珠保溫砂漿是以玻化微珠為輕質骨料與玻化微珠保溫膠粉料按照一定的比例攪拌均勻混合而成的用于外墻內外保溫的一種新型無機保溫砂漿材料。玻化微珠保溫砂漿具有優異的保溫隔熱性能和防火耐老化性能、不空鼓開裂、強度高、現場施工加水攪拌即可使用。

Vitrified beads insulation mortar on vitrified beads for light aggregate and vitrified beads insulation powder material in accordance with certain proportion of mixture and stir well to internal and external wall thermal insulation material of a new type of inorganic thermal insulation mortar。 Vitrified beads insulation mortar with excellent heat preservation and heat insulation and fire resistance to aging performance, no empty drum cracking, high intensity, site construction and water mixing can be used。


一、玻化微珠保溫砂漿施工工藝

A, vitrified beads insulation mortar construction technology


1、先將水倒入容器中,再加入粉料,按1kg粉劑:約0.7-0.9kg水的配合比,混合后用電動攪拌器攪拌成均勻、無顆粒的膏糊狀,產品靜置3-5分鐘后,再次攪拌均勻后即可使用。

1, the first to add water into the container, add powder, press 1 kg powder: about 0。7-0。9 kg of water mixture, mix with an electric mixer mixing into a smooth, no particles as paste, products stand for 3-5 minutes, after mix can be used again。


2、用刮刀均勻抹于工作面上,待其24小時干固后,再進行下一道刮涂,同樣用刮刀均勻抹于工作面上再抹平;每次刮涂應保持厚度在15mm-20mm為宜(單次最大厚度不超過35mm),待達到設計厚度要求后,自然養護3-7天即可進行下道工序。

2, with scraper, even put on in the work surface after the 24 hours of dry solid, then under a blade coating, wipe again with scraper even put on in the same job surface flat; Each blade coating thickness shall be maintained at 15 mm to 20 mm advisable (single biggest thickness no more than 35 mm), thickness to meet the design requirement, natural curing 3 to 7 days can be next working procedure.


二、玻化微珠保溫砂漿施工注意事項:

Second, vitrified beads insulation mortar construction matters needing attention:


1、玻化微珠保溫砂漿宜在5℃-40℃的環境下使用。

1, vitrified beads insulation mortar should be at 5 ℃ and 40 ℃ under the environment of use.


2、施工前必須先確認基面的垂直度及平整度。

2, before construction must first confirm the verticality and smoothness.


3、如果膠漿表面已干結,應將結皮剔去不用。

3, if the mucilage surface is hard and crust should be picked。


4、切忌把已干結的膠漿加水混合再用。

4, avoid by all means have stem node of the mucilage water mixed with。


5、面磚飾面系統的增強層可選擇使用耐堿加強型網格布或熱鍍鋅鋼絲網。

5, brick veneer system enhancement layer can choose to use alkali enhanced grid cloth or hot dip galvanized wire mesh.


6、玻化微珠保溫砂漿施工前基層需做界面處理。

6, vitrified beads insulation mortar construction at the grass-roots level to be done before processing interface.


7、攪拌時請使用低速攪拌器。

7, mixing, please use the low speed mixer.


8、玻化微珠保溫砂漿運輸時注意避免重壓。

8, the transport of vitrified beads insulation mortar take care to avoid stress。

以下產品    詳細咨詢18832673888   進入網站查看詳細情況

 

保溫砂漿 www.vfeqvs.com

硅酸鹽板

阿里巴巴華東官網

阿里巴巴華東分店 huadong.1688.com


最新评论
請先登錄才能進行回復登錄
  • 电话直呼

    • 18831662333
    • 銷售經理 :
    • 售前咨詢 :
    • 售前咨詢 :
    • 售后服務 :
    • 售后服務 :
    • 合同簽訂/施工方案 :
    • 合同簽訂/施工方案 :
  • 掃一掃,關注旺鋪

2019年信誉网赚网站 网赚好一点的平台 什么网赚最赚现在 网赚彩票群可靠吗 任我赢机器人 上海快3走势图 19年正规网赚项目 青春510网赚论坛 2019免费挂机网赚项目 2019挂机国内网赚软件